Unsaturated Polyester Resin AP114
    
بازدید: 3397
    

AP114 is an unsaturated polyester resin based on terephthalic acid. This resin is dissolved in styrene.

 

Applications and Fabrication Techniques

  • Recommended for most commercial FRP fabrication processes such as: hand lay- up, spray-up, pultrusion, stone craft , SMC & BMC
  • Mastic manufacturing industries

مشخصه میزان واحد
Colour <2 gardner
Density, 25°C/77°F 1.08 ± 0.04 g/cm3
Dynamic Viscosity, 25°C/77°F 300-600 cP
Styrene Content 30-40 %
Acid Value Max. 20 mg KOH/g
Shelf Life, Dark, 25°C/77°F 4 months

Typical properties are not to be construed as specifications. 

عنوان وزن
Resin Temperature 25°C/77°F
Catalyst 1 (phr)(2)
Cobalt octoate1% 1 (phr)
Gel Time (min.) 5-20 (3)

Use MEKP 9.9 % Active, O (e.g. AKZO M60 or equivalent peroxide system) as catalyst and Cobalt octoat-1%
phr = parts per hundred resin molding compound
Gel time would be adjustable as request

مشخصه میزان واحد استاندارد روش آزمون
Tensile Strength (MPa) Min. 70.0 ASTM D638
Tensile Elongation (%) Min. 3.5 ASTM D638
Tensile Modulus (GPa) Min. 3.0 ASTM D638
Flexural Strength (MPa) Min. 120.0 ASTM D790
Flexural Modulus (GPa) Min. 3.0 ASTM D790
Heat Distortion Temperature (6) °C Min. 65.0 ASTM D 648 /ISO 75
Barcol Hardness (7) Min. 38.0 ASTM D2583

Handling and Storage Consideration:
This resin should be stored indoors in the original, unopened and undamaged packaging, in a dry place at temperatures between 5°C and 30°C. The shelf life of styrene containing unsaturated polyester resins will be significantly reduced when exposed to light and/or higher temperatures.

Safety:
This resin contains ingredients which could be harmful if mishandled. Contact with skin and eyes should be avoided and necessary protective equipment and clothing should be worn.



  نظرات
دیدگاه های ارسال شده توسط شما، پس از تایید مدیر سایت در وب سایت منتشر خواهد شد.
پیام هایی که حاوی تهمت یا افترا باشد منتشر نخواهد شد.
پیام هایی که به غیر از زبان فارسی یا غیر مرتبط با خبر باشد منتشر نخواهد شد.